成品钢种 | A1 | A2 |
饱和度 | WO3≥99.95% | WO3≥99.9% |
灼损 | ≤0.5% | ≤0.5% |
药剂学设计 | Content(≤%)量 | Content(≤%)含铁 |
Al | 0.0005 | 0.0010 |
As | 0.0010 | 0.0150 |
Bi | 0.0001 | 0.0010 |
Ca | 0.0010 | 0.0060 |
Cd | 0.0010 | 0.0010 |
Co | 0.0010 | 0.0010 |
Cr | 0.0010 | 0.0010 |
Cu | 0.0003 | 0.0010 |
Fe | 0.0010 | 0.0030 |
K | 0.0010 | 0.0010 |
Mg | 0.0007 | 0.0010 |
Mn | 0.0010 | 0.0010 |
Mo | 0.0020 | 0.0200 |
Na | 0.0010 | 0.0040 |
Ni | 0.0007 | 0.0010 |
P | 0.0007 | 0.0020 |
Pb | 0.0001 | 0.0010 |
S | 0.0007 | 0.0050 |
Sb | 0.0005 | 0.0010 |
Si | 0.0010 | 0.0040 |
Sn | 0.0002 | 0.0010 |
Ti | 0.0010 | 0.0010 |
V | 0.0010 | 0.0010 |
均值粒度分布FSSS | 12-20μm | 0.6-1.8μm |